钢—聚乙烯醇纤维混凝土与锈蚀钢筋粘结性能研究

发布时间：2018-02-19 22:13

  本文关键词： 钢—聚乙烯醇纤维混凝土 锈蚀率 粘结性能 粘结强度系数　出处：《水电能源科学》2017年06期 　论文类型：期刊论文

【摘要】：为研究混杂纤维混凝土与锈蚀钢筋粘结性的关系,通过电化学加速锈蚀,获取4组不同钢筋锈蚀率(0~6.89%)的钢—聚乙烯醇纤维混凝土试件。采用中心拉拔试验,得到不同锈蚀率情况下钢筋与混杂纤维混凝土的粘结强度,分析锈蚀率、混杂纤维体积率对钢筋与混凝土粘结性能的影响,并根据试验结果提出了混杂纤维混凝土粘结强度系数和滑移值系数与钢筋锈蚀率之间的数学关系式。结果表明,在一定范围内混杂纤维体积率越大,钢筋与混凝土之间的粘结性能越好,粘结强度随着锈蚀率的升高呈现先增加后下降的趋势。
[Abstract]:In order to study the relationship between the adhesion of hybrid fiber reinforced concrete and corroded steel bar, four groups of steel-polyvinyl alcohol fiber reinforced concrete specimens with different corrosion rate of steel bar and polyvinyl alcohol fiber concrete were obtained by electrochemical accelerated corrosion. The bond strength of steel bar and hybrid fiber concrete is obtained under different corrosion rate. The effect of corrosion rate and hybrid fiber volume ratio on bond performance of steel bar and concrete is analyzed. Based on the experimental results, the mathematical relations between the bond strength coefficient and slip value coefficient of hybrid fiber concrete and the corrosion rate of steel bar are presented. The results show that the volume ratio of hybrid fiber increases in a certain range. With the increase of corrosion rate, the bond strength increases first and then decreases with the increase of corrosion rate.
【作者单位】： 苏州科技大学土木工程学院;苏州科技大学江苏省结构工程重点实验室;
【基金】：国家自然科学基金项目(51508368) 江苏省结构工程重点实验室资助项目(ZD1205)
【分类号】：TU528

【相似文献】

相关期刊论文 前5条

1 王蓬亮;;维·尼·纶[J];赣江经济;1981年04期

2 王德松，李淑敏，马劲松，徐端夫;聚乙烯醇纤维和维尼纶纤维增强水泥石的研究[J];河北轻化工学院学报;1996年03期

3 ;高强高模聚乙烯醇纤维协作项目取得成果[J];科技和产业;2002年10期

4 林水东;李莉;王琪;;熔纺聚乙烯醇纤维对水泥砂浆的增强增韧作用[J];高分子材料科学与工程;2011年05期

5 ;[J];;年期

相关硕士学位论文 前1条

1 王海波;聚乙烯醇纤维（维纶）增强砂浆性能的研究[D];北京工业大学;2003年

，

本文编号：1518110