水工超高掺粉煤灰混凝土设计与试验研究

发布时间：2018-08-28 15:59

【摘要】：尽管目前水工高掺量粉煤灰混凝土的设计方法很多,但受已有的设计理念、设计方法及现行规范的限制和束缚,水工常态混凝土的粉煤灰掺量很难超过50%,这一状况就与国外形成了较大差距。本文介绍了一种水工超高掺粉煤灰混凝土配合比的设计新方法,采用以普通硅酸盐水泥+80%粉煤灰拌制的混凝土,其各项性能均达到水工混凝土C_(180)40要求,与采用普通方法设计的中热水泥+35%粉煤灰同强度等级混凝土相比,水化温升更低,干缩更小,抗裂性能更优,且总体成本更低,为水工混凝土进一步展现其完整含义,实现特征归真开辟了途径。
[Abstract]:Although there are many design methods of high content fly ash concrete in hydraulic engineering at present, it is restricted and bound by the existing design ideas, design methods and current codes. The content of fly ash in hydraulic normal concrete is difficult to exceed 50, which is a big gap with foreign countries. In this paper, a new design method of super high mixing ratio of hydraulic concrete with fly ash is introduced. The concrete mixed with 80% fly ash of ordinary Portland cement has all the properties that meet the requirement of C _ (180) 40 of hydraulic concrete. The hydration temperature rise is lower, the dry shrinkage is smaller, the crack resistance is better, and the overall cost is lower than that of the medium heat cement 35% fly ash with the same strength grade concrete designed by the common method, which further shows its complete meaning for hydraulic concrete. The realization of features to truth opens up a way.
【作者单位】： 中国能源建设集团有限公司;葛洲坝集团试验检测有限公司;
【基金】：中国能源建设集团有限公司科技项目(CEEC12-KJ02) 中国葛洲坝集团股份有限公司科技项目(2012KJ-03)
【分类号】：TV431

【相似文献】

相关期刊论文 前10条

1 周孝正,邹一宝;掺粉煤灰混凝土早期抗裂性能初步探讨[J];水利水电技术;1984年10期

2 赵庚,刘敬廉;对粉煤灰混凝土抗裂指标的初步探讨[J];水利水电技术;1986年08期

3 岳耀真,丁宝瑛;掺粉煤灰混凝土早期抗裂性的有限元分析[J];水力发电;1991年01期

4 李述民;张亚伟;张英;;高寒地区水利工程原状粉煤灰混凝土施工特点初探[J];东北水利水电;1993年09期

5 张希清,宋少民,刘娟红;粉煤灰混凝土表面性能研究[J];粉煤灰综合利用;2002年02期

6 孔德玉;掺粉煤灰混凝土生命周期评价方法初探[J];浙江工业大学学报;2002年02期

7 张海虹;刘延军;陶春梅;刘占明;朱炳喜;;连云港市烧香河北闸拆建工程粉煤灰混凝土应用技术[J];粉煤灰综合利用;2008年06期

8 李述民;张英;;粉煤灰混凝土在高寒地区水利工程中应用[J];水利天地;1993年04期

9 惠荣炎,黄国兴;粉煤灰混凝土依时性变形的试验研究[J];水利水电技术;1992年08期

10 黄木佳,郑汉滨;粉煤灰混凝土在潮州供水枢纽工程中的应用及效果[J];广东建材;2004年05期

相关硕士学位论文 前3条

1 王馨苑;用于防渗抗冻装配式渠道的粉煤灰混凝土配方试验研究[D];宁夏大学;2016年

2 杨e，

本文编号：2209893