干燥方式对白炭黑性能的影响

发布时间：2018-03-16 19:15

  本文选题：白炭黑　切入点：湿法研磨　出处：《中国粉体技术》2017年03期 　论文类型：期刊论文

【摘要】：利用冷冻、喷雾、真空、烘箱干燥等4种干燥方式对对湿法研磨后的白炭黑浆料进行处理,研究干燥方式对白炭黑粒径、吸油值、比表面积和微观形貌等理化性能的影响。结果表明:研磨干燥后的白炭黑,中位径d_(50)由9.6μm减小到110 nm以下,吸油值(DBP)与比表面积(BET)均小于研磨前;冷冻干燥样品的中位径d_(50)减小为73 nm,吸油值(2.15 mL/g)以及比表面积(144 m~2/g)与原样最为接近。
[Abstract]:Four drying methods, freezing, spray, vacuum and oven drying, were used to treat the white carbon black slurry after wet grinding, and the effect of drying method on the particle size and oil absorption value of silica was studied. The results showed that the average diameter of silica after grinding and drying decreased from 9.6 渭 m to less than 110 nm, and the oil absorption value (DBP) and specific surface area (BET) were lower than those before grinding. The median diameter of freeze-dried samples was reduced to 73 nm, the oil absorption value was 2.15 mL / g and the specific surface area was 144 mL / g).
【作者单位】： 华东理工大学超细材料制备与应用教育部重点实验室;
【基金】：国家自然科学基金项目,编号:91534202;91534122 上海市基础重点研究项目,编号:15JC1401300 国家国际科技合作专项项目,编号:2015DFA51220
【分类号】：TQ127.2

【相似文献】

中国期刊全文数据库 前10条

1 张婉婷;陈佳琳;张灵枝;;不同干燥方式对单丛茶抗氧化能力影响研究[J];中国茶叶加工;2011年01期

2 刘长虹;曹斌辉;钱志海;;不同干燥方式对酵子储存品质影响的研究[J];食品科技;2010年04期

3 于静静;毕金峰;丁媛媛;;不同干燥方式对红枣品质特性的影响[J];现代食品科技;2011年06期

4 解红霞;陈相艳;王文亮;曲静然;程安玮;弓志青;;不同干燥方式对杨梅中总多酚和花青素含量的影响[J];食品科技;2014年02期

5 许牡丹;杨雯;马占儒;;干燥方式对枣粉生产的可行性研究[J];食品科技;2012年01期

6 狄化p，

本文编号：1621281